UBESTA 3014U
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | UBE Industries, Ltd. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nk8US6_UBESTA-3014U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity (Injection) |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.90 | % | |
| Flow | 0.90 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 47.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Flexural Stress | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 2.90 | IEC 60250 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 90-A123A-80 | Teknor Apex Company | PVC, Flexible | APEX® |
| apilon 52® D 30 L | API SpA | TPU-Polyester | apilon 52® |
| Electrafil® PA6/6 GF10 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Plyophen 23057 | Durez Corporation | Phenolic | Plyophen |
| Novalloy-S S5230 | PlastxWorld Inc. | PC+ABS | Novalloy-S |