Applications: For shopping and grocery bags, perforated rolls, trash bags, and industrial liners. Characteristics: Bimodal blown film grade having high tensile and impact strength, good stiffness and barrier properties with a wide molecular weight distribution for easy processing. Performs well under heavy load conditions. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 9.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD 1 | 990 | MPa | ASTM D882 |
| 1% secant, MD 2 | 930 | MPa | ASTM D882 |
| 1% secant, TD 3 | 1140 | MPa | ASTM D882 |
| 1% secant, TD 4 | 1030 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture 5 | 75.0 | MPa | ASTM D882 |
| MD : Fracture 6 | 70.0 | MPa | ASTM D882 |
| TD : Fracture 7 | 55.0 | MPa | ASTM D882 |
| TD : Fracture 8 | 65.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture 9 | 520 | % | ASTM D882 |
| MD : Fracture 10 | 560 | % | ASTM D882 |
| TD : Fracture 11 | 560 | % | ASTM D882 |
| TD : Fracture 12 | 550 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709 | ||
| -- 13 | 250 | g | ASTM D1709 |
| -- 14 | 330 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD 15 | 11 | g | ASTM D1922 |
| MD 16 | 17 | g | ASTM D1922 |
| TD 17 | 78 | g | ASTM D1922 |
| TD 18 | 39 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 126 | °C | ASTM D1525 19 |
| Additional Information |
|---|
| Film fabrication condition: extruder @55mm, die @90mm, die gap 1.35mm, temperature 200°C, output 55kg/hr, BUR 4.9, thickness 25µm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 3 to 5 |
| Note Message | |
|---|---|
| 1 . | With stabilizer |
| 2 . | without stabilizer |
| 3 . | With Stabilizer |
| 4 . | Without stabilizer |
| 5 . | With stabilizer |
| 6 . | Without stabilizer |
| 7 . | With stabilizer |
| 8 . | Without stabilizer |
| 9 . | With stabilizer |
| 10 . | Without stabilizer |
| 11 . | With stabilizer |
| 12 . | Without stabilizer |
| 13 . | With stabilizer |
| 14 . | Without stabilizer |
| 15 . | With stabilizer |
| 16 . | Without stabilizer |
| 17 . | With stabilizer |
| 18 . | Without stabilizer |
| 19 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8240-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Comtrex Flexible PVC® 71XCF | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | Comtrex Flexible PVC® |
| Ethylplus 625 MD | Fainplast Compounds S.r.l | MDPE | Ethylplus |
| Hylon® N1240MHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LUVOCOM® 50/GF/10/TF/18/SI/2/GY5 | Lehmann & Voss & Co. | PC | LUVOCOM® |