Carbo-Rite™ M-2530
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Carbo-Rite™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NiaTLV_Carbo-Rite-M-2530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Carbo-Rite™ M-2530 is a carbon black-filled HIPS compound available in pellet form. Carbo-Rite™ M-2530 solves a wide range of static decay, static shielding and electromagnetic shielding problems. Features: Cost-effective ESD protection, consistent performance, recyclable, durable Applications: Thermoformed trays, Tape & Reel Carrier Tape, Extruded conductive HIPS sheet |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 to 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1360 | MPa | ASTM D638 |
| Tensile Strength (Break) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 16 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 62.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | 5.0E+4 | ohms | ESD S11.11 |
| Volume Resistivity 2 | 5.0E+6 | ohms·cm | ESD S11.12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content | Internal Method | ||
| Anions Cl- | < 0.0100 | µg/cm² | |
| Anions NO3- | ND | ||
| Anions PO4- | ND | ||
| Anions SO4- | ND | ||
| Outgassing | Internal Method | ||
| MMA | 0.00 | µg/cm² | |
| Styrene | 290 | µg/cm² | |
| Toluene | 12.0 | µg/cm² |
| Note Message | |
|---|---|
| 1 . | 12% RH |
| 2 . | 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L ASL015 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| RTP 205 TFE 15 Z | RTP Company | Nylon 66 | RTP |
| Rotec® ABS TS 15/02 | ROMIRA GmbH | ABS | Rotec® ABS |
| SUSTAMID 6G M | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| BESTNYL SE60VI01AH | Triesa Plastics | Nylon 66 | BESTNYL |