Generic Polyester Alloy - Glass\Inorganic
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nhx4ew_Generic-Polyester-Alloy---Glass-Inorganic.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Polyester Alloy - Glass\Inorganic This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 2.00 - 2.10 | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 - 0.88 | g/cm³ | ISO 60 |
| Molding Shrinkage (23°C) | 0.025 - 0.56 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 50.0 - 65.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 13500 - 17100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 90.0 - 150 | MPa | ISO 178 |
| Compressive Stress (23°C) | 173 - 175 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 7.4 - 17 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 200 - 250 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 198 - 250 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 110 - 220 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.5E+12 - 5.5E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 5.5E+13 - 6.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 23 | kV/mm | IEC 60243-1 |
| Dissipation Factor (23°C) | 0.015 - 0.050 | IEC 60250 | |
| Comparative Tracking Index | 550 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 105 - 108 | °C | |
| Mold Temperature | 170 - 173 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Polyester Alloy - Glass\InorganicThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tefzel® 2195 | DuPont Fluoropolymers | ETFE | Tefzel® |
| Telcar® TL-1269A | Teknor Apex Company | TPE | Telcar® |
| Latilub 66-01M G/50 | LATI S.p.A. | Nylon 66 | Latilub |
| POLIMAXX 320PC | IRPC Public Company Limited | SAN | POLIMAXX |
| UTEC 6540 | Braskem | UHMWPE | UTEC |