UBE Nylon 5034 UC2
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBE Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NhvUGm_UBE-Nylon-5034-UC2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBE NYLON 5034 UC2 is a Nylon Clay Hybrid material. This PA6/6.6 Copolyamide contains exfoliated Montmorillonite platelets incorporated into the polymeric structure. It is produced by UBE's unique, patented pretreatment and polymerization technology. The material offers enhanced mechanical and barrier properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 80.9 | MPa | ISO 527-2 |
| Fracture | 50.8 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.9 | % | ISO 527-2 |
| Fracture | 150 | % | ISO 527-2 |
| Flexural Modulus | 3350 | MPa | ISO 178 |
| Flexural Stress | 121 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 144 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 58.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 192 | °C | ISO 3146 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Notched Izod Impact, ISO 180, 23°C, Notch A: 51 J/mMolecular Ratio, PA6/PA6.6: 80/20 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3570 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ACCUTECH™ HP0336W10L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Carbotex K-20UV | Kotec Corporation | PC | Carbotex |
| HONES® PBT GF30 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PBT | HONES® |
| Kostrate® EDGE HB | Plastic Selection Group, Inc. | TP, Unspecified | Kostrate® EDGE |