Lustran® ABS 288
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NhhcIu_Lustran-ABS-288.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran ABS 288 is a very high-flow injection molding grade of ABS (acrylonitrile butadiene styrene) with good impact strength and high gloss. It is intended for use in a wide range of applications, particularly in thin-walled components for telecommunications, office equipment, consumer and other office products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 30 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 38.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | ISO 180 | ||
| -34°C | 13 | kJ/m² | ISO 180 |
| 23°C | 24 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 9.00 | J | ASTM D3763 |
| 23°C, Total Energy | 40.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm span | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 4.00mm span | 76.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ISO 306/A120 |
| -- | 94.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 95 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 266 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 70% of the injection pressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® TP10-GP1 | Toray Resin Company | ABS | Toyolac® |
| Ad-Tech Urethanes LUC-4101 | Ad-Tech Plastic Systems Corp. | PUR, Unspecified | Ad-Tech Urethanes |
| Allen ABS AX7/LXS | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Europrene Latice® 1150 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Huafon JF-S-8120 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |