Pibiflex® 3560
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nh551H_Pibiflex-3560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Pibiflex® 3560 is a Thermoplastic Copolyester Elastomer (TPC-ET) material. It is available in Europe, Latin America, or North America for injection molding. Primary attribute of Pibiflex® 3560: REACH Compliant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 25.0 | cm³/10min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 35 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 18.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 850 | % | ASTM D638 |
| Flexural Modulus | 55.0 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 60.0 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 195 | °C | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | 1.0E+13 | ohms·cm | |
| 100°C | 1.0E+11 | ohms·cm | |
| Dielectric Strength (2.00 mm) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.30 | ||
| 100 kHz | 4.25 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 6.0E-3 | ||
| 100 kHz | 0.015 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 20 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fatigue Resistance | 0.1/300 | kCycles | ASTM D1052 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 283 HEC | RTP Company | Nylon 66 | RTP |
| Mirathane™ M70 | Miracll Chemicals Co., Ltd. | TPU-Polyether | Mirathane™ |
| Styrolution PS 416N | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| SUMIKASUPER® LCP E6008L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Sylvin 9067-70 NATURAL | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |