SUPRAN® LFT PA A1350
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SAMBARK |
| Trademark: | SUPRAN® LFT PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ngo7Db_SUPRAN-LFT-PA-A1350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% long glass fiber reinforced polyamide 66. High Stiffness, superior mechanical balanced & heat stable. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D648 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 237 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.9 | % | ASTM D638 |
| Flexural Modulus | 13500 | MPa | ASTM D790 |
| Flexural Strength | 302 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 250 | J/m | |
| 23°C | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 256 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 3240EH | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PPcompound |
| NAXELL™ PC117MH | MRC Polymers, Inc. | PC | NAXELL™ |
| Braskem PE GM 5010 T2 B | Braskem | HDPE | Braskem PE |
| INNOPOL® PP CS 2-3302 TO BU | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| Karina GRAY PVC COMPOUND 902-18/71-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |