EXCELINK 2800B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | JSR Corporation |
| Trademark: | EXCELINK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nghbo1_EXCELINK-2800B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EXCELINK 2800B is a thermoplastic vulcanized rubber (TPV) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of EXCELINK 2800B are:
The typical application field of EXCELINK 2800B is: sealing application |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/10.0 kg | 300 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 84 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (100% Strain) | 4.10 | MPa | ISO 37 |
| Tensile Stress - Across Flow (Yield) | 6.90 | MPa | ISO 37 |
| Tensile Elongation - Across Flow (Break) | 540 | % | ISO 37 |
| Compression Set (70°C, 22 hr) | 52 | % | ISO 815 |
| Additional Information |
|---|
| Oil Resistance(IRM903), JIS K6258, 24hours, 80°C: 32%Oil Resistance(IRM903), JIS K6258, 24hours, 24°C: 8% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultrason® S 3010 MR UN | BASF Corporation | PSU | Ultrason® S |
| Hostacom EKC 330NA | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Lucet® N145-LD | LG Chem Ltd. | Acetal (POM) Copolymer | Lucet® |
| OTECH ALLOY OTO9141LSZH - Riser Insulation | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| LEXAN™ 201R resin | SABIC Innovative Plastics | PC | LEXAN™ |