Ultramid® 8333G HI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ngh02t_Ultramid-8333G-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8333G HI is a 33% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. It is also available in heat stabilized (Ultramid 8333G HI HS) and/or pigmented versions. Applications Ultramid 8333G HI is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.34 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| 24 hr | 0.90 | -- | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Saturation | 5.5 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.5 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.5 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 9200 | -- | MPa | |
| 23°C | 9300 | 4610 | MPa | |
| 121°C | 2660 | -- | MPa | |
| Tensile Strength | ||||
| Break, 23°C | 152 | 90.0 | MPa | ASTM D638 |
| Break, 23°C | 145 | 90.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 3.5 | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 8820 | 9500 | MPa | ASTM D790 |
| 23°C | 8000 | 4830 | MPa | ASTM D790 |
| 65°C | 4040 | 3290 | MPa | ASTM D790 |
| 90°C | 3280 | 3250 | MPa | ASTM D790 |
| 121°C | 3040 | 2970 | MPa | ASTM D790 |
| 23°C | 7200 | 5030 | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 310 | 297 | MPa | ASTM D790 |
| 23°C | 241 | 124 | MPa | ASTM D790 |
| 65°C | 130 | 110 | MPa | ASTM D790 |
| 90°C | 105 | 100 | MPa | ASTM D790 |
| 121°C | 89.0 | 90.0 | MPa | ASTM D790 |
| 23°C | 215 | 120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 20 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 78 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| 23°C | 240 | -- | J/m | ASTM D256 |
| -40°C | 14 | -- | kJ/m² | ISO 180 |
| 23°C | 21 | -- | kJ/m² | ISO 180 |
| Drop Impact Resistance (23°C) | 4.88 | -- | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 2.4E-5 | -- | cm/cm/°C | |
| Transverse | 8.4E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.800 mm | 105 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 95.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.800 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 43 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 100 Hz | 3.60 | -- | ||
| 1 MHz | 3.40 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.010 | -- | ||
| 1 MHz | 0.010 | -- | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 GV 30 HW | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Xuchuan XCW-SP30 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| BP RPP 2012 T BLK | Buckeye Polymers, Inc. | PP Homopolymer | BP |
| Greenflex® FD 20 F | Versalis S.p.A. | EVA | Greenflex® |
| LEXAN™ EXL5689 resin | SABIC Innovative Plastics | PC | LEXAN™ |