Sup-tech B705EX
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NgXTMn_Sup-tech-B705EX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech B705EX is a Polyamide 6 (Nylon 6) product filled with 25% glass fiber. It can be processed by extrusion or injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 1.5E-3 to 5.0E-3 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 1.0 | % | |
| Saturation, 23°C | 5.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 85.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 3.0 | % | DIN 53452 |
| Flexural Modulus | 3800 | MPa | DIN 53457 |
| Flexural Stress | 100 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 190 | °C | |
| Melting Temperature | 220 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torayca® 3101T-20V | Toray Resin Company | Nylon 66 | Torayca® |
| Cogegum® GFR/365 | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| DJSilicone NE--T-2/NE-T-2U (general) | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| DuraFlex 889-2 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| KPOL-NYLON K-NY6/40CF | KPOL Chem Co. | Nylon 66/6 | KPOL-NYLON |