Kepital® F20-51
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NgLK5n_Kepital-F20-51.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium viscosity grade, black color, for weather resistance purpose. It has stability on UV light, and so good at out-door use. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 10 | g/10 min | ASTM D1238 |
| -- | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.00 mm | 2.0 | % | ASTM D955 |
| 3.00 mm | 2.0 | % | |
| Water Absorption (Equilibrium, 23°C, 60%) | 0.22 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 60.0 | MPa | ASTM D638 |
| Yield, 23°C | 62.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 60 | % | ASTM D638 |
| Nominal Tensile Strain at Break | 25 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2650 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 88.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 116 | °C | ASTM D648 |
| Melting Temperature | 165 | °C | |
| CLTE - Flow (20 to 80°C) | 1.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+16 | ohms | ASTM D257 |
| -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 19 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® Electro 242-2 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| ULTZEX™ 15100C | Prime Polymer Co., Ltd. | LLDPE | ULTZEX™ |
| Karina IVORY PVC COMPOUND -E 90900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Idemitsu PS MS500 | Idemitsu PS | PS (GPPS) | Idemitsu PS |
| Hostacom ERC 346N C21451 | LyondellBasell Industries | PP Copolymer | Hostacom |