Orevac® T 9304
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Orevac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ng3Y1m_Orevac-T-9304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OREVAC® T 9304 is a random terpolymer of ethylene, vinyl acetate and maleic anhydride made by high-pressure radicalar polymerization process. As an ethylene copolymer, OREVAC® T 9304 is compatible with PE in all proportions, and with most other ethylene copolymers. Vinyl acetate brings softness, flexibility and polarity, maleic anhydride gives reactivity, leading to versatile adhesive properties to polar and non polar substrates. As a result of high-pressure polymerisation in tubular reactor, OREVAC® T 9304 exhibits high transparency (low haze). Applications OREVAC® T 9304 is compatible with most tackifying resins and waxes and can be used for hot melt adhesives formulations. OREVAC® T 9304 is also suitable to produce thermo-adhesive films for solid substrates like PA, PET & PU films, aluminium foils, fiber mats, foams... OREVAC® T 9304 can also be used as a tie layer between polyethylene and polyamide in blown film coextrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.5 to 9.3 | g/10 min | ASTM D1238, ISO 1133 |
| Vinyl Acetate Content | 23.5 to 26.5 | wt% | |
| Maleic Anhydride Content | 1600 | ppm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ring and Ball Softening Point | 150 | °C | ASTM E28 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 2.80 mm, Compression Molded) | 82 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break, 2.80 mm, Compression Molded 1 | 26.0 | MPa | ASTM D638 |
| Break, 2.80 mm, Compression Molded | 26.0 | MPa | ISO 527-2/5A/50 |
| Tensile Elongation | |||
| Break, 2.80 mm, Compression Molded 2 | 600 to 900 | % | ASTM D638 |
| Break, 2.80 mm, Compression Molded | 600 to 900 | % | ISO 527-2/5A/50 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 43.0 | °C | ISO 306/A, ASTM D1525 3 |
| Melting Temperature | 80.0 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 230 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics 200 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Garaflex™ O 9777-A2 NATURAL | AlphaGary | TPE | Garaflex™ O |
| Grivory® HT1V-4 HY black 9205 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Hostacom EKC 425N C11323 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| PERLEX® R251 | A. Schulman Europe | PC | PERLEX® |