CRYSTALADD® HM-237E

Category:	HDPE , High Density Polyethylene
Manufacturer:	Ravago Manufacturing Americas, LLC
Trademark:	CRYSTALADD®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ne3XOF_CRYSTALADD-HM-237E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
MINERAL AND NUCLEATOR MASTERBATCH HM-237E is an additive concentrate containing both a Mineral additive for resin displacement and as a process aide; plus a highly efficient Nucleator. Nucleation and mineral combinations in LLDPE can improve film properties and yield rates. In HDPE blow molding HM-237E can reduce cycle time and achieve better control over shrinkage characteristics. In injection molding applications improvements in the dimensional stability and reductions in cycle time can be attained. Key Features: Designed to be added to polyethylene film, extrusion, blow molding and injection molding resins. Also used to improve properties/processing in PP resins Excellent dispersion of additive and Mineral Uniform concentration of additives in concentrate form. Masterbatch pellet form for ease of addition and feeding into extrusion equipment Directions for Use: HM-237E is added to HDPE / LLDPE (and PP) at 2.5% to achieve improved crystallization for faster cooling, lower warpage especially between different colors. Achieve more uniform crystal sizes as the PE cools for improved gloss and barrier properties. FDA Compliance: The components of this product are compliant with FDA requirements up to 9% LD by weight. Please consult with the FDA regulations for specific application requirements.

Message

MINERAL AND NUCLEATOR MASTERBATCH

HM-237E is an additive concentrate containing both a Mineral additive for resin displacement and as a process aide; plus a highly efficient Nucleator. Nucleation and mineral combinations in LLDPE can improve film properties and yield rates. In HDPE blow molding HM-237E can reduce cycle time and achieve better control over shrinkage characteristics. In injection molding applications improvements in the dimensional stability and reductions in cycle time can be attained.

Key Features:

Designed to be added to polyethylene film, extrusion, blow molding and injection molding resins.

Also used to improve properties/processing in PP resins

Excellent dispersion of additive and Mineral

Uniform concentration of additives in concentrate form.

Masterbatch pellet form for ease of addition and feeding into extrusion equipment

Directions for Use:

HM-237E is added to HDPE / LLDPE (and PP) at 2.5% to achieve improved crystallization for faster cooling, lower warpage especially between different colors. Achieve more uniform crystal sizes as the PE cools for improved gloss and barrier properties.

FDA Compliance:

The components of this product are compliant with FDA requirements up to 9% LD by weight. Please consult with the FDA regulations for specific application requirements.

General Information
Uses	Masterbatch
Forms	Pellets
Processing Method	Blow Molding Extrusion Film Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.85	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	12	g/10 min	ASTM D1238

Additional Information	Nominal Value	Unit	Test Method
Mineral Content	75	%	ASTM D297
Nucleating Agent	4.0	%	Internal Method
Polymer Base	HDPE

Resin Grade	Manufacturer	Category	Trademark
Algoflon® F 5/S	Solvay Specialty Polymers	PTFE	Algoflon®
HiFill® PP GB20	Techmer Engineered Solutions	PP, Unspecified	HiFill®
IPC PP 4800H	International Polymers Corporation	PP Homopolymer	IPC PP
LG PMMA ID178	LG MMA Corp.	Acrylic (PMMA)	LG PMMA
Osterlene® HD-.057-959	Osterman & Company	HDPE	Osterlene®