ALCOM® HTC 300/1 WT1056-10LD
| Category: | Copolyester , Copolyester |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® HTC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NdKGFL_ALCOM-HTC-300-1-WT1056-10LD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® HTC 300/1 WT1056-10LD is a Copolyester product filled with filler. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® HTC 300/1 WT1056-10LD include automotive and lighting applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 45.0 | MPa | |
| -- | 45.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 110 | % | |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 70.0 | MPa | |
| 3.5% Strain | 55.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 85 | kJ/m² | |
| -40°C | 10 | kJ/m² | |
| -20°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | No Break | ||
| -20°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 650 | °C | |
| 2.00 mm | 650 | °C | |
| 3.00 mm | 650 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 1(Total, 1000 µm) | 56.8 | % | ISO 13468 |
| Haze 2(1000 µm) | 95 | % | ISO 13468 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Half Power Angle - T(Y) 3 | |||
| 1.00 mm | 51.0 | ° | |
| 4.00 mm | 65.0 | ° |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | A, 2° |
| 2 . | Ill. A, 2° |
| 3 . | A, 2° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Melamine Melamine | Saudi Basic Industries Corporation (SABIC) | Mel Phenolic | SABIC® HDPE |
| Hapflex™ 595-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Ingeo™ AW 240D | NatureWorks® LLC | PLA | Ingeo™ |
| InnoTuf® HP-1085A | Innovative Polymers, Inc. | TSU-Ester | InnoTuf® |
| ISOTHANE® 1070A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |