Salflex 810CI
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Salflex Polymers Ltd. |
| Trademark: | Salflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NdDHIi_Salflex-810CI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Salflex 810CI is a polypropylene copolymer (PP Copoly) product, which contains a 10% glass fiber reinforced material. It can be processed by injection molding and is available in North America. The application fields of Salflex 810CI include automobile industry and industrial application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2140 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 1990 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 91.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Ash Content, ISO 3451/1A: 10% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 195 - 225 | °C | |
| Front Temperature | 195 - 225 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 195 - 215 | °C | |
| Mold Temperature | 24.0 - 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT014 | Sasol Polymers | LDPE | Sasol Polymers PE |
| Witcom PA66 6G/3L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| ACCUTECH™ HP0339M30CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Globalprene® 3537 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| LUVOCOM® 1100-8944 | Lehmann & Voss & Co. | PESU | LUVOCOM® |