Romiloy®8150 is an acrylonitrile-styrene-acrylate PC (ASA PC) material,. This product is available in Europe and is processed by extrusion or injection molding. Romiloy®The main features of the 8150 are:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 240°C/5.0 kg | 20 | g/10 min | ISO 1133 |
| 260°C/5.0 kg | 35 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Slow |
| Injection instructions |
|---|
| Back Pressure: <10%Holding Pressure: LowScrew Rotation Speed: slow |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 200 - 240 | °C | |
| Cylinder Zone 2 Temp. | 200 - 240 | °C | |
| Cylinder Zone 3 Temp. | 200 - 240 | °C | |
| Cylinder Zone 4 Temp. | 200 - 240 | °C | |
| Cylinder Zone 5 Temp. | 200 - 240 | °C | |
| Melt Temperature | < 250 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DURACON® SF-10 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Halene H M5002L | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| KOPLA PP KPE1020 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |
| LNP™ LUBRICOMP™ RP002 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Petro Rabigh PP FY2011E | Rabigh Refining & Petrochemical Co. | PP Homopolymer | Petro Rabigh PP |