GELOY™ EXGY0070 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NcXaUc_GELOYEXGY0070resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 8.8 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 7.1 | g/10 min | ASTM D1238 |
| 280°C/3.8 kg | 7.2 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 9.60 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.40 - 0.70 | % | Internal method |
| Flow : 3.20mm | 0.40 - 0.70 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.75 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2360 | MPa | ASTM D638 |
| -- 3 | 2400 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 43.0 | MPa | ASTM D638 |
| Yield 5 | 46.0 | MPa | ASTM D638 |
| Yield | 45.8 | MPa | ISO 527-2/50 |
| Fracture 6 | 36.0 | MPa | ASTM D638 |
| Fracture 7 | 37.0 | MPa | ASTM D638 |
| Fracture | 36.5 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 8 | 2.5 | % | ASTM D638 |
| Yield 9 | 2.7 | % | ASTM D638 |
| Yield | 2.8 | % | ISO 527-2/50 |
| Fracture 10 | 27 | % | ASTM D638 |
| Fracture 11 | 26 | % | ASTM D638 |
| Fracture | 36 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 12 | 2450 | MPa | ASTM D790 |
| -- 13 | 2380 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 64.0 | MPa | ISO 178 |
| Yield, 50.0mm span 14 | 74.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 15(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 35 | J/m | ASTM D256 |
| 23°C | 210 | J/m | ASTM D256 |
| -30°C 16 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 17 | 15 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 3.00 | J | ASTM D3763 |
| 23°C, Total Energy | 36.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 97.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 18 | 98.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 19 | 84.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525 20 |
| -- | 95.0 | °C | ISO 306/B50 |
| -- | 99.0 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 8.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 9.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 93 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 215 - 250 | °C | |
| Middle Temperature | 220 - 255 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Nozzle Temperature | 220 - 255 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 60.0 - 85.0 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa | |
| Screw Speed | 30 - 80 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | 50 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | Type 1, 50mm/min |
| 8 . | Type 1, 5.0 mm/min |
| 9 . | Type 1, 50mm/min |
| 10 . | Type 1, 5.0 mm/min |
| 11 . | Type 1, 50mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 2.0 mm/min |
| 14 . | 1.3 mm/min |
| 15 . | 80*10*4 sp=62mm |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 mm |
| 19 . | 80*10*4 mm |
| 20 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 977 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| CP PRYME® Polycarbonate PC300FRU | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Huafon JF-W-AH6035 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Luran® S 797SE | Styrolution | ASA | Luran® S |
| O'Tech OW 649 AFR | O'Tech Corporation | PVC, Unspecified | O'Tech |