OmniTech™ PBSA GR30
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniTech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nc56hf_OmniTech-PBSA-GR30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Fiber Reinforced, PBT/ASA |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 177 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 249 to 277 | °C | |
| Front Temperature | 249 to 277 | °C | |
| Nozzle Temperature | 249 to 277 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman ABS 730 | Shuman Plastics, Inc. | ABS | Shuman ABS |
| TECHNYL® C 216 V40 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Chemraz XCD | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| EXCELINK 1700B | JSR Corporation | TPV | EXCELINK |
| Lucent PP CPP-120 | Lucent Polymers, Inc. | PP Homopolymer | Lucent PP |