SABIC® LDPE 2501TH00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nbe1R3_SABIC-LDPE-2501TH00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® LDPE 2501TH00 is an additive free clarity grade, which combines excellent film processability with very good optical properties and stiffness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 200 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 200 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : 45 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Total Energy Impact (50 µm, Blown Film) | 0.750 | J | ASTM D4272 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 45 µm, blown film | 2.8 | N | ISO 6383-2 |
| TD : 50 µm, blown film | 2.8 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Clarity | 0.0150 | V | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 20 | g | Internal method |
| Re-blocking | g | Internal method |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PFA 345 | DuPont Fluoropolymers | PFA | Teflon® PFA |
| Sindustris PBT TE5001GU | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| SKYBOND® 700 | Industrial Summit Technology Co. | API | SKYBOND® |
| OmniLon™ PA6/6 MS2 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| TECHNYL® A 217 NATURAL S | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |