UBE Nylon 7034 B Datasheet,Nylon 612,UBE Engineering Plastics, S.A.-SHANGHAI SUSHENG

Message
UBE NYLON 7034 B is a high viscosity PA6/12 Copolyamide. It is suitable for applications with indirect food contact according FDA and EU regulations. The grade can be used for cast film and blown film (air or water cooled).

General Information
Features	Workability, good Definition, high Compliance of Food Exposure High shrinkage Viscosity, High
Uses	Films cast film
Appearance	Natural color
Forms	Particle
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	1.11	g/cm³	ISO 1183

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	1.0	ASTM D1894
With Self-Static	1.0	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD	425	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield	23.0	MPa	ASTM D882
Fracture	97.0	MPa	ASTM D882
Tensile Elongation - MD (Break)	600	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	201	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	155		ASTM D523
Haze	1.0	%	ASTM D1003

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Molecular Ratio, PA6/PA12: 80/20Oxygen Permeability, ASTM D3985: 85 ml/m²/daySurface Resistivity, UBE Method: >1e15 ohmExtractable Content, JIS K6810: <1.0 wt%Relative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.8Water Vapor Permeability, JIS Z0208: 85 g/m²/dayPiercing Strength, JAS P1019: 850 N/mmPiercing Elongation, JAS P1019: 14.5 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle: <20 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle: <10 hole/0.04 m²

Additional Information

The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Molecular Ratio, PA6/PA12: 80/20Oxygen Permeability, ASTM D3985: 85 ml/m²/daySurface Resistivity, UBE Method: >1e15 ohmExtractable Content, JIS K6810: <1.0 wt%Relative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.8Water Vapor Permeability, JIS Z0208: 85 g/m²/dayPiercing Strength, JAS P1019: 850 N/mmPiercing Elongation, JAS P1019: 14.5 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle: <20 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle: <10 hole/0.04 m²

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom PP5120C B1	Spartech Polycom	PP, Unspecified	Spartech
DENIFORM 3010	Vamp Tech	Acetal (POM) Copolymer	DENIFORM
Epocast 8623-A/Hardener 946	Huntsman Advanced Materials	Epoxy	Epocast
HANWHA LDPE 5322	Hanwha Chemical	LDPE	HANWHA LDPE
Sylvin 9077-90 White 1315	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin

Category:	Nylon 612 , Polyamide 612
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NbF67A_UBE-Nylon-7034-B.pdf
PRICE:	Order Products email sales@su-jiao.com