| Solef® 32008 PVDF copolymer is a low viscosity and very flexible grade for Wire&Cable applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 to 3.0 | % | |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 2.00 mm) | 47 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 2.00 mm) | 100 to 300 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 14.0 to 35.0 | MPa | |
| Break, 23°C, 2.00 mm | 14.0 to 30.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 10 to 12 | % | |
| Break, 23°C, 2.00 mm | 350 to 600 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 to 0.30 | ||
| vs. Itself - Static | 0.20 to 0.40 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel) | 5.00 to 15.0 | mg | ASTM D4060 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C, 4.00 mm) | No Break | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -28.0 | °C | ASTM D4065 |
| Vicat Softening Temperature | 75.0 | °C | ASTM D1525 5 |
| Melting Temperature | 165 to 170 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 125 to 130 | °C | ASTM D3418 |
| CLTE - Flow (0 to 40°C) | 1.3E-4 to 1.5E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat | ASTM E968 | ||
| 23°C | 1200 | J/kg/°C | |
| 100°C | 1600 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.20 | W/m/K | ASTM C177 |
| Crystallization Heat | 15.0 to 22.0 | J/g | ASTM D3417 |
| Heat of Fusion | 15.0 to 22.0 | J/g | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 kHz) | 7.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.00 mm) | 48 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Type IV, 1.0 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 2 m/s, Partial Break |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® Q121 TR20 | Razin™ Engineering Plastics | PP Homopolymer | Razalen® |
| RANPELEN SFC-851 | Lotte Chemical Corporation | PP Terpolymer | RANPELEN |
| 3M™ Dyneon™ Fluoroplastic THV 221AZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| Kalix® 9950 | Solvay Specialty Polymers | HPPA | Kalix® |
| KEBAFLEX® E D 50.1 | BARLOG plastics GmbH | TPV | KEBAFLEX® |