RTP 1685
| Category: | PAS , Polyarylsulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nb3NEG_RTP-1685.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24100 | MPa | ASTM D638 |
| Tensile Strength | 179 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 17200 | MPa | ASTM D790 |
| Flexural Strength | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 213 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 2mil/in.Tensile Elongation, ASTM D-638: 1-2% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 343 - 399 | °C | |
| Middle Temperature | 343 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Mold Temperature | 121 - 177 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) M/HI-G | A. Schulman Europe | ABS | POLYMAN® |
| Miramid® H3CW | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Electrafil® 02056 BKN | Techmer Engineered Solutions | PP, Unspecified | Electrafil® |
| Hyundai EP PA66 LD610 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| I. Stern 870E | I. STERN & CO. INC. | PS (HIPS) | I. Stern |