LNP™ LUBRICOMP™ KL001 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NaOBT3_LNP-LUBRICOMP-KL001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KL001 is a compound based on Acetal Copolymer resin containing 5% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KL-4010 Product reorder name: KL001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.44 | g/cm³ | ASTM D792 |
| -- | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.3 | % | |
| Across Flow : 24 hr | 2.3 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2620 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 55.2 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 |
| Break | 52.4 | MPa | ASTM D638 |
| Break | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.9 | % | ASTM D638 |
| Yield | 11 | % | ISO 527-2 |
| Break | 34 | % | ASTM D638 |
| Break | 30 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3450 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 13.8 | MPa | ASTM D790 |
| -- | 70.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.38 | ||
| vs. Itself - Static | 0.18 | ||
| Wear Factor - Washer | 22.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 5.3 | J/m | ASTM D256 |
| 23°C 2 | 48 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D4812 |
| 23°C 3 | 1000 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.30 | J | ASTM D3763 |
| -- | 0.900 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 158 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 149 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 112 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 96.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next PC CXF-01NC | Next Polymers Ltd. | PC | Next PC |
| BJB Polyurethane TC-640 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Boda BDT246-1EP | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| APEX® 157-V | Teknor Apex Company | PVC, Flexible | APEX® |
| Hyrene® PSCRY 1.5 | Entec Polymers | PS (GPPS) | Hyrene® |