Skyrol® SP65
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NaGgg6_Skyrol-SP65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SP65 is a transparent film with excellent handling characteristics and widely used in flexible packaging applications. SP65 is corona treated on one side. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | |||
| Flow : 150°C, 30 min, 0.00900 mm | 1.8 | % | Internal Method |
| Flow : 150°C, 30 min, 0.0120 mm | 1.8 | % | Internal Method |
| Flow : 150°C, 30 min, 0.0230 mm | 1.6 | % | ASTM D955 |
| Flow : 150°C, 30 min, 0.0360 mm | 1.5 | % | ASTM D955 |
| Across Flow : 150°C, 30 min, 0.00900 mm | 0.50 | % | Internal Method |
| Across Flow : 150°C, 30 min, 0.0120 mm | 0.60 | % | Internal Method |
| Across Flow : 150°C, 30 min, 0.0230 mm | 0.60 | % | ASTM D955 |
| Across Flow : 150°C, 30 min, 0.0360 mm | 0.60 | % | ASTM D955 |
| Surface Tension | ASTM D2578 | ||
| Corona Treated : 9.0 µm | 54 | mN/m | |
| Corona Treated : 12.0 µm | 52 | mN/m | |
| Corona Treated : 23.0 µm | 52 | mN/m | |
| Corona Treated : 36.0 µm | 54 | mN/m | |
| Untreated : 9.0 µm | 46 | mN/m | |
| Untreated : 12.0 µm | 46 | mN/m | |
| Untreated : 23.0 µm | 46 | mN/m | |
| Untreated : 36.0 µm | 46 | mN/m |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.30 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Dynamic 4 | 0.40 | ||
| vs. Itself - Dynamic 5 | 0.50 | ||
| vs. Itself - Static 6 | 0.40 | ||
| vs. Itself - Static 7 | 0.50 | ||
| vs. Itself - Static 8 | 0.50 | ||
| vs. Itself - Static 9 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 9.0 µm | 296 | MPa | |
| MD : Yield, 12 µm | 303 | MPa | |
| MD : Yield, 23 µm | 255 | MPa | |
| MD : Yield, 36 µm | 248 | MPa | |
| TD : Yield, 9.0 µm | 255 | MPa | |
| TD : Yield, 12 µm | 255 | MPa | |
| TD : Yield, 23 µm | 248 | MPa | |
| TD : Yield, 36 µm | 228 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 9.0 µm | 110 | % | |
| MD : Break, 12 µm | 110 | % | |
| MD : Break, 23 µm | 130 | % | |
| MD : Break, 36 µm | 130 | % | |
| TD : Break, 9.0 µm | 120 | % | |
| TD : Break, 12 µm | 120 | % | |
| TD : Break, 23 µm | 120 | % | |
| TD : Break, 36 µm | 120 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 9.00 µm | 161 | ||
| 12.0 µm | 162 | ||
| 23.0 µm | 162 | ||
| 36.0 µm | 160 | ||
| Transmittance | ASTM D1003 | ||
| 9.00 µm | 90.0 | % | |
| 12.0 µm | 90.0 | % | |
| 23.0 µm | 90.0 | % | |
| 36.0 µm | 90.0 | % | |
| Haze | ASTM D1003 | ||
| 9.00 µm | 3.1 | % | |
| 12.0 µm | 2.9 | % | |
| 23.0 µm | 3.5 | % | |
| 36.0 µm | 4.7 | % |
| Note Message | |
|---|---|
| 1 . | 23 µm |
| 2 . | 36 µm |
| 3 . | 23 µm |
| 4 . | 12 µm |
| 5 . | 9 µm |
| 6 . | 36 µm |
| 7 . | 12 µm |
| 8 . | 9 µm |
| 9 . | 23 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven F-605 | Propilven, S.A. | PP Homopolymer | Propilven |
| Monprene® CP-28177 | Teknor Apex Company | TPE | Monprene® |
| Arnite® TV4 230 | DSM Engineering Plastics | PBT | Arnite® |
| Epic Urethane S7445 | Epic Resins | PUR, Unspecified | Epic Urethane |
| Leona™ 53G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |