Mecoline IS RDX 1221 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NaD6oY_Mecoline-IS-RDX-1221-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound is an ideal choice for the insulation of heat-resistant wires and cables for general applications in railway systems, nuclear power stations, engine compartments and other areas. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (160°C/10.0 kg) | 7.0 | g/10 min | ISO 1133 |
| pH | 4.5 | IEC 60754-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 1 | IEC 540 | ||
| Elongation under load | 20 | % | |
| Residual elongation | 10 | % | |
| Temperature Index | 225 | °C | ASTM D2863 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | 2.00 | µS/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | 0 | % | IEC 754-1 |
| Toxicity | 2.00 | EN 50305 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 160 to 170 | °C | |
| Extruder Screw L/D Ratio | >24.0:1.0 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 49 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 2 | 17.0 | MPa | |
| -- 3 | > 8.00 | MPa | |
| Tensile Strain | IEC 811-1-1 | ||
| Break 4 | 350 | % | |
| Break 5 | > 600 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (158°C, 168 hr) | 10 | % | IEC 811-1-2 |
| Change in Tensile Strain at Break in Air (158°C, 168 hr) | -2.0 | % | IEC 811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (20°C, 50 Hz) | 5.00 | ASTM D150 | |
| Dissipation Factor (20°C, 50 Hz) | 0.025 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 130 to 140 | °C | |
| Cylinder Zone 2 Temp. | 150 to 160 | °C | |
| Cylinder Zone 3 Temp. | 160 to 170 | °C | |
| Cylinder Zone 4 Temp. | 160 to 170 | °C | |
| Cylinder Zone 5 Temp. | 160 to 170 | °C | |
| Adapter Temperature | 160 to 170 | °C | |
| Die Temperature | 160 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | at 200°C/15min/0.2 MPa |
| 2 . | After crosslinking |
| 3 . | Before crosslinking |
| 4 . | After crosslinking |
| 5 . | Before crosslinking |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| G-Lex B52A003 | Gas Authority of India Limited | HDPE | G-Lex |
| LARIPUR® LPR 5520 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| PROXESS 1806S3 | Braskem | LLDPE | PROXESS |
| StarFlex® 7092-1003 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |
| Durethan® BKV 50 H EF DUS022 900116 | LANXESS GmbH | Nylon 6 | Durethan® |