VENYL UG360 is a 30% glass fibre reinforced polyamide 66 with characteristics of resistance to wear and friction for injection moulding. APPLICATIONS VENYL UG360 has been developed especially for very demanding applications in automotive industry and electrical parts requiring excellent friction characteristics and wear resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.49 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.70 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.40 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9700 | 6650 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 155 | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 9200 | 6500 | MPa | ISO 178 |
| Flexural Stress | 220 | 175 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 31 | 39 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 196 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DELPET™ 982J | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| FRAGOM XLC/125 R | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| EL-Lene™ H6430BM | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| ICORENE® 3440 | ICO Polymers SA, A Division of A. Schulman | PE Copolymer | ICORENE® |
| Sylvin 9053-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |