Generic PPE+TPE
| Category: | PPE+TPE , Polyphenylene Ether + TPE |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NYXxQE_Generic-PPE-TPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPE+TPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 - 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 5.1 - 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.40 - 1.1 | % | ASTM D955 |
| Transverse flow : 23°C | 0.33 - 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.059 - 0.23 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 70 - 93 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture, 23°C | 8.50 - 27.4 | MPa | ASTM D638 |
| Fracture, 23°C | 8.75 - 23.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 93 - 310 | % | ASTM D638 |
| Fracture, 23°C | 90 - 230 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 37.7 - 163 | MPa | ASTM D790 |
| 23°C | 27.0 - 720 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 7.00 - 46.0 | N/mm | ISO 6383-1 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| UL Temperature Rating | 80 - 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 1.5E+15 - 5.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 3.8E+14 - 3.9E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 21 - 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.60 - 3.00 | ASTM D150 | |
| 23°C | 2.90 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 1.0E-3 - 7.4E-3 | ASTM D150 | |
| 23°C | 1.5E-3 - 0.030 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 743 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 725 - 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 24 - 29 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 80.0 | °C | |
| Drying Time | 6.0 | hr | |
| Cylinder Zone 1 Temp. | 200 - 205 | °C | |
| Cylinder Zone 3 Temp. | 235 - 245 | °C | |
| Cylinder Zone 5 Temp. | 235 - 246 | °C | |
| Melt Temperature | 235 - 246 | °C | |
| Die Temperature | 235 - 246 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+TPEThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Caltex PP M540SB | GS Caltex | PP Impact Copolymer | Caltex PP |
| DOW™ VLDPE DFDB-1088 NT | The Dow Chemical Company | VLDPE | DOW™ VLDPE |
| Haysite Plastics H330 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| LNP™ LUBRICOMP™ DFL36XXJ compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Petrothene® NA952 | LyondellBasell Industries | LDPE | Petrothene® |