Grilamid® 2S 25 W 20 HL X black 9992
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NYQX9G_Grilamid-2S-25-W-20-HL-X-black-9992.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid® 2S 25 W 20 HL X black 9992 is a Polyamide 610 (Nylon 610) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or profile extrusion. Important attributes of Grilamid® 2S 25 W 20 HL X black 9992 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.03 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 1.8 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 3.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 50.0 | 35.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 750 | 450 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 50.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 15 | kJ/m² | |
| 23°C | No Break | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 125 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/A |
| Maximum Use Temperature | Internal Method | |||
| Long Term | 130 | -- | °C | |
| Short Term | 160 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA610-HIP, EH, 22-007 | -- | ISO 1874 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 215 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-4 | -- | cm/cm/°C | |
| Transverse | 1.5E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | 36 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® EVA 1803 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| Eltex® TUB 350-HM00 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | Eltex® |
| GTPO™ 8101 | S&E Specialty Polymers, LLC | TPO (POE) | GTPO™ |
| 3M™ Dyneon™ PTFE Compound TF 6419 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Durethan® B 30 S FN30 000000 | LANXESS GmbH | Nylon 6 | Durethan® |