LNP™ THERMOTUF™ DF008EI compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NXW2Mp_LNPTHERMOTUFDF008EIcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF DF008EI is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, High Impact. Also known as: LNP* THERMOTUF* Compound DF-1008 EM HI MR Product reorder name: DF008EI |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Transverse flow : 24 hours | 0.30 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.33 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.040 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12600 | MPa | ASTM D638 |
| -- | 11100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 132 | MPa | ASTM D638 |
| Yield | 129 | MPa | ISO 527-2 |
| Fracture | 132 | MPa | ASTM D638 |
| Fracture | 130 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.2 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2 |
| Fracture | 2.2 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10600 | MPa | ASTM D790 |
| -- | 10100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 2 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 840 | J/m | ASTM D4812 |
| 23°C 3 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 23.1 | J | ASTM D3763 |
| -- | 7.69 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 134 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 135 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 4.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 D TFE 10 | RTP Company | Nylon 6/12 | RTP |
| PRIMALLOY® A1800 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| SUPREME HIPS SH825 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| AVP™ ZLL30CP | SABIC Innovative Plastics | PC | AVP™ |
| Fainplast PVC RKI 01298/W-UV | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |