SEETEC LLDPE UF414
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | SEETEC LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NWTHpV_SEETEC-LLDPE-UF414.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UF414 is manufactured by Unipol process technology. UF414 has good mechanical properties and good processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 39.2 | MPa | |
| TD : Break, 40 µm, Blown Film | 34.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 780 | % | |
| TD : Break, 40 µm, Blown Film | 800 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 49.0 | kN/m | |
| TD : 40.0 µm | 88.3 | kN/m |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 72 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GA-3028 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Spartech Polycom X02435 | Spartech Polycom | PPE | Spartech |
| Akulon® S223-HG6 | DSM Engineering Plastics | Nylon 66 | Akulon® |
| Chiao Fu PA66 MD212LST NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| KOPA® KN333G15V0BK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |