Sindustris ABS LLG810W
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NWBoW0_Sindustris-ABS-LLG810W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LLG810W is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LLG810W are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 41.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 20 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 69 | J/m | |
| -30°C, 6.40 mm | 49 | J/m | |
| 23°C, 3.20 mm | 150 | J/m | |
| 23°C, 6.40 mm | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 106 | °C | |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 5 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°) | 30 | ASTM D2457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 68.6 to 88.3 | MPa | |
| Screw Speed | < 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiten® 115P | ITEN INDUSTRIES | Phenolic | Resiten® |
| FLEXAREN® 14006 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| Geon™ Vinyl Flexible A5DUB | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ESPRENE EPDM 6101 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| LNP™ THERMOCOMP™ DF008ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |