Trexprene® A55SCI
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NTWfde_Trexprene-A55SCI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A55SCI is a heat and UV stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This grade also contains a "Slip Additive" for improved scratch/mar resistance and anti-wear properties. This material is available as a custom pre-colored compound and is intended primarily for interior trim applications. This compound can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 to 0.970 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 62 to 68 | ||
| Shore A, 5 sec | 59 to 65 | ||
| Shore A, 15 sec | 55 to 61 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Across Flow : 100% Strain | 1.90 | MPa | |
| Flow : 100% Strain | 3.50 | MPa | |
| Tensile Stress 2 | ISO 37 | ||
| Across Flow : Yield | 4.90 | MPa | |
| Flow : Yield | 4.20 | MPa | |
| Tensile Elongation 3 | ISO 37 | ||
| Across Flow : Break | 560 | % | |
| Flow : Break | 250 | % | |
| Tear Strength 4 | ISO 34-1 | ||
| Across Flow | 23 | kN/m | |
| Flow | 19 | kN/m | |
| Compression Set | |||
| 125°C, 70 hr | 44 | % | ASTM D395B |
| 125°C, 70 hr 5 | 44 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (125°C, 1000 hr) | 17 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (125°C, 1000 hr) | -20 | % | ISO 188 |
| Change in Shore Hardness in Air (Shore A, 125°C, 1000 hr) | 3.0 | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -50.0 | °C | ASTM D746 |
| Type B | -50.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 19 | mm/min | ISO 3795 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Accelerated Weathering Duration 6 | AATCC > 4 | ||
| Ozone Resistance 7(40°C) | 0 Rating | ISO 1431-1 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | Filtered Xenon per FLTM BO 116-01, 2481.6 kJ/m² |
| 7 . | 100 pphm, Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ 8030NHS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| VECTRA® MT1310 | Celanese Corporation | LCP | VECTRA® |
| ExxonMobil™ PP8244E1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Gallonprene® GP420-3501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Sylvin 9466-50D Natural | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |