| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NTKFoC_Kingfa-FRHIPSV-0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa FRHIPSV-0 is a High Impact Polystyrene material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa FRHIPSV-0 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3 | 2100 | MPa | ASTM D790 |
| Flexural Strength 4 | 37.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 72.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 182 to 205 | °C | |
| Middle Temperature | 205 to 230 | °C | |
| Front Temperature | 215 to 240 | °C | |
| Processing (Melt) Temp | 220 to 245 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 5.00 to 15.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3908T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| YUNGSOX® PP 5060 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| CERTENE™ PBM-12 | Muehlstein | PP Impact Copolymer | CERTENE™ |
| Asaflex™ 810 | AKelastomers | SBS | Asaflex™ |
| Karina STRAW PVC COMPOUND 751-38/117-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |