TECHNYL® A 216 V25 NATURAL R
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NRsrQ8_TECHNYLA216V25NATURALR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 216 V25 Natural R is a polyamide 66, reinforced with 25% of glass fiber, for injection moulding. This grade offers an excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8400 | 6300 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 165 | 120 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 3.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7300 | 5000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 57 | 87 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.5 | 15 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | IEC 60112 | |||
| Solution a | 600 | 600 | V | IEC 60112 |
| Solution B | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.6 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 275 - 285 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Mold Temperature | 70 - 100 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUCOMP™ ABS801L | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| Braskem PP RP 225M | Braskem | PP Random Copolymer | Braskem PP |
| Ferro PP LPP40BK16HB-WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| INELEC PA66CF10 | Infinity LTL Engineered Compounds | Nylon 66 | INELEC |
| LNP™ LUBRILOY™ DF2041 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |