TPX® MX002
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NRDx5y_TPXMX002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPX®MX002 is a polymethylpentene copolymer (PMP copolymer) material,. This product is available in Europe or the Asia-Pacific region. The processing methods are: blow molding, extrusion or injection molding. TPX®The main characteristics of MX002 are: hardness. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.835 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 | % | ASTM D955 |
| Transverse flow | 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 62 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 785 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 20.0 | MPa | ASTM D638 |
| 23°C | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 60 | % | ASTM D638 |
| Flexural Modulus (23°C) | 641 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 24.8 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 |
| Melting Temperature | 222 | °C | |
| CLTE - Flow | 3.8E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 63 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.12 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.463 | ASTM D542 | |
| Clarity | 93.0 | ASTM D1746 | |
| Haze | 0.90 | % | ASTM D1003 |
| Additional Information |
|---|
| Unnotched Izod Impact, ASTM D256, 23°C: 98 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2199 X 117875 A | RTP Company | PEI | RTP |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2001Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Bormed™ RB801CF-01 | Borealis AG | PP Random Copolymer | Bormed™ |
| Europrene® N 3945 | Versalis S.p.A. | NBR | Europrene® |
| LUVOCOM® 1105/WT106 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |