Order Products : sales@su-jiao.com
Garaflex™ 131-T NAT
| Category: | PVC+NBR , Polyvinyl Chloride + NBR |
| Manufacturer: | AlphaGary |
| Trademark: | Garaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NQ5o3N_Garaflex-131-T-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GARAFLEX 131-T IS A OIL RESISTANT, LEAD FREE UNIT SOLE COMPOUND. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 to 1.17 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 55 to 61 | ||
| Shore A, 15 sec | 43 to 49 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | |||
| -- 1 | 1.4 | ||
| -- 2 | 0.93 | ||
| -- 3 | 0.92 | ||
| -- 4 | 1.6 | ||
| Taber Abrasion Resistance | |||
| loss, 1000 cycles | 0.400 | % | |
| loss, 5000 cycles | 1 | % | |
| Ross Flex (-29°C, 6.35 mm) | 48000 | ASTM D1052 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain, 1.91 mm) | 1.86 | MPa | ASTM D412 |
| Tensile Strength (1.91 mm) | 8.27 | MPa | ASTM D412 |
| Tensile Elongation (Break, 1.91 mm) | 380 | % | ASTM D412 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 143 | °C | |
| Middle Temperature | 149 | °C | |
| Front Temperature | 154 | °C | |
| Nozzle Temperature | 154 | °C | |
| Processing (Melt) Temp | 154 to 160 | °C |
| Note Message | |
|---|---|
| 1 . | Dry Surface - Wood |
| 2 . | Wet Surface - Wood |
| 3 . | Wet Surface - Aluminum |
| 4 . | Dry Surface - Aluminum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 83MF10 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| TEKANATE™ G7038 | Mando Advanced Materials Co., Ltd. | PC | TEKANATE™ |
| Ultrason® P 3010 | BASF Corporation | PPSU | Ultrason® P |
| Evoprene™ COGEE 682 | AlphaGary | SEBS | Evoprene™ COGEE |
| EXCELINK 1101B | JSR Corporation | TPV | EXCELINK |