VENYL UC406
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NPnoyK_VENYL-UC406.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UC406 is a 45 % mineral / carbon fibre reinforced polyamide 66 lubrified intended for Injection moulding. APPLICATIONS VENYL UC406 has been developed especially for demanding applications for good resistant final parts and rigidity combined with good stiffness and heat stabilization. Products requiring excellent combination between thermal and mechanical properties. VENYL UC406 is available only in black (VENYL UC406). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.70 to 0.90 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 113 | MPa | ISO 527-2 |
| Flexural Modulus | 8000 | MPa | ISO 178 |
| Flexural Stress | 165 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 31 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+5 | ohms·cm | DIN 53482 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 295 to 310 | °C | |
| Middle Temperature | 290 to 300 | °C | |
| Front Temperature | 285 to 295 | °C | |
| Nozzle Temperature | 275 to 310 | °C | |
| Mold Temperature | 85.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PET EN230 | Guangdong Shunde Shunyan New Material Co., Ltd. | PET | Sunny® |
| Trithene® TS 9022 | Petroquimica Triunfo | LDPE | Trithene® |
| UNITIKA Nylon 6 A1030GFL | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| Escorene™ Ultra UL 40028EM1 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| HOPELEX PC-1220R | Lotte Chemical Corporation | PC | HOPELEX |