XENOY™ XL1339 resin
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NPg66w_XENOY-XL1339-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Data generated in BOZ labs. High heat grade for nonchemical resistance required applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (265°C/1.2 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.50 to 0.80 | % | |
| Across Flow | 0.50 to 0.80 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | |
| Equilibrium, 23°C | 0.70 | % | |
| Equilibrium, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2100 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 3 | 50.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 4 | 50.0 | MPa | ASTM D638 |
| Break | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 6 | 110 | % | ASTM D638 |
| Break | 70 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2100 | MPa | ASTM D790 |
| -- 8 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 94.5 | MPa | ASTM D790 |
| Poisson's Ratio | 0.40 | ASTM D638 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 16.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -40°C | 220 | J/m | ASTM D256 |
| -30°C | 250 | J/m | ASTM D256 |
| -20°C | 600 | J/m | ASTM D256 |
| 0°C | 670 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -40°C 12 | 15 | kJ/m² | ISO 180/1A |
| -30°C 13 | 25 | kJ/m² | ISO 180/1A |
| -20°C 14 | 35 | kJ/m² | ISO 180/1A |
| -10°C 15 | 38 | kJ/m² | ISO 180/1A |
| 23°C 16 | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 17 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 18 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 125 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 105 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 130 | °C | ISO 306/B50 |
| -- | 135 | °C | ISO 306/B120 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.9E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.18 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 2.0E-3 | ||
| 60 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 249 to 271 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 254 to 271 | °C | |
| Processing (Melt) Temp | 260 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 430Y MH1 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Exxtral™ Performance Polyolefin CMV206 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Jampilen RP128M | Jam Polypropylene Company | PP Terpolymer | Jampilen |
| Sylvin 9604-90 Yellow 405 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ARLEN™ C230N | Mitsui Chemicals America, Inc. | Nylon 6T | ARLEN™ |