Edistir® RC 600
| Category: | PS (MIPS) , Medium Impact Polystyrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Edistir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NPKD3x_Edistir-RC-600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Special medium impact polystyrene grade exhibiting very high gloss. This grade is designed to be used in injection moulding where is required an excellent surface finish. Designation: Thermoplastics ISO 2897-PS-I,M,O88-O6-04-18 Applications Examples of application are consumer electronics, office furnishings, internal components of refrigerators, sanitary and household wares, jewel and cosmetic boxes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1950 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 29.0 | MPa | ISO 527-2/50 |
| Fracture | 24.5 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 40 | % | ISO 527-2/50 |
| Flexural Stress 1 | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 70 | J/m | ISO 180/4A |
| -30°C | 3.5 | kJ/m² | ISO 180/1A |
| 23°C | 5.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ISO 306/A50 |
| -- | 88.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 65 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 3.0E-4 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastics ISO 2897-PS-I,M,088-06-04-18 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 250 | °C | |
| Mold Temperature | 40.0 - 75.0 | °C |
| Injection instructions |
|---|
| Predrying normally not required |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400.5 N | RTP Company | PESU | RTP |
| Colorite Rigid PVC 2600 NAT | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Grilon® TSG-30/4 H black 9839 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Plenco 01506 (Injection) | Plastics Engineering Co. | Polyester, TS | Plenco |
| PENTAMID A GV25 H blue 5010/1 | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |