Bionate® II 55D
| Category: | PC+TPU , Polycarbonate + TPU |
| Manufacturer: | DSM Biomedical Inc. |
| Trademark: | Bionate® II |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NP6qcU_Bionate-II-55D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bionate® II 55D is a Polycarbonate + TPU (PC+TPU) product. It can be processed by extrusion or injection molding and is available in North America. Applications of Bionate® II 55D include medical/healthcare and food contact applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) 1 | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 to 2.3 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.54 | % | ASTM D750 |
| Average Molecular Weight | 231000 | Mw | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 56 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 61.8 | MPa | ASTM D1708 |
| Tensile Stress | ASTM D1708 | ||
| 50% Strain | 13.6 | MPa | |
| 100% Strain | 18.1 | MPa | |
| 300% Strain | 49.0 | MPa | |
| Tensile Elongation (Break) | 370 | % | ASTM D1708 |
| Flexural Modulus - 1% Secant | 95.1 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain) | 3.52 | MPa | ASTM D790 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.46 | ASTM D1894 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 11.0 | mg | ASTM D1044 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 1.00 | °C | ASTM E1356 |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| Melting Temperature | 180 | °C | ASTM E1356 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.71 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 191 to 218 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 177 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | 224°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tufpet PBT N2100 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| Clyrell EC5080 | PolyMirae | TPO (POE) | Clyrell |
| Hytrel® 3078FG | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina BLACK PVC COMPOUND -E 807-48/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax TYC 007P E C13101 | LyondellBasell Industries | PP Copolymer | Hifax |