4TECH 9S22130 is a Standard Flow 30% Glass Fibre Reinforced PPO |
General Information | |
---|---|
Filler / Reinforcement |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.28 | g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus (23°C) | 10000 | MPa | ISO 527-2/5 |
Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2/5 |
Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 11 | kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating (1.60 mm) | HB | UL 94 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 70.0 - 90.0 | °C | |
Drying Time | 2.0 - 3.0 | hr | |
Suggested Max Moisture | 0.020 | % | |
Processing (Melt) Temp | 270 - 300 | °C | |
Mold Temperature | 80.0 - 120 | °C | |
Injection Rate | Slow-Moderate | ||
Holding Pressure | 60.0 - 120 | MPa | |
Screw Speed | 250 | rpm |
Injection instructions |
---|
Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Sylvin 6227-83 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
Vacuum Cast V-855 A/B | BJB Enterprises, Inc. | PUR, Unspecified | Vacuum Cast |
Cevian®-V VGR30 | Daicel Polymer Ltd. | ABS | Cevian®-V |
Elastron® G G500.A70.N.PA | Elastron USA, Inc. | SEBS | Elastron® G |
KEBATRON® PPS C2040G5 | BARLOG plastics GmbH | PPS | KEBATRON® |