Wellamid® GFX1743-BK1(PTFE)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NOe8pI_Wellamid-GFX1743-BK1-PTFE-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Wellamid® GFX1743-BK1(PTFE) is a Polyamide 66 (Nylon 66) material filled with 43% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Primary attribute of Wellamid® GFX1743-BK1(PTFE): Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.70 to 1.1 | % | |
| Flow : 23°C | 0.20 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 180 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 255 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 138254 A NS | RTP Company | Polyester Alloy | RTP |
| SABIC® STAMAX 60YK270 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| Tecomid® NA40 GR40 NL RM | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| TEREZ PA 6 7510 GF 25 MF 15 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Unichem 4511-34 WHITE | Colorite Polymers | PVC, Flexible | Unichem |