Lotader® 3430

Category:	EMA , Ethylene Methyl Acrylate Copolymer
Manufacturer:	Arkema
Trademark:	Lotader®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NNmaPv_Lotader-3430.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LOTADER® 3430 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.

Applications
LOTADER® 3430 is a versatile adhesive for extrusion coating or lamination, designed as:

Concentrate to be used in dry blend with LDPE. LOTADER® 3430 improves adhesion of LDPE on aluminium foils, metallized or primerized films.

Ready for use resin to be used pure. LOTADER® 3430 gives excellent adhesion on substrates likes aluminium foil, metallized plastics, paper, board, PE and some plastic films like BOPP.

Coextrusion tie layer for PE/PA in extrusion coating process.

LOTADER® 3430 is also a coupling agent for mineral filled compounds such as halogen free flame retardant wires and cables, a compatibilizer for polyamide/polyolefin blends and a modifier for polyamides.

General Information
Features	Good Adhesion High Melt Stability Terpolymer
Uses	Adhesives Coating Applications Laminates
Forms	Pellets
Processing Method	Coextrusion Extrusion Coating Laminating

Physical	Nominal Value	Unit	Test Method
Density	0.940	g/cm³	ISO 1183, ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ASTM D1238, ISO 1133
Methyl Acrylate Content	15.0	wt%
Maleic Anhydride Content	3.1	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	30		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	12.0	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	750	%	ASTM D638, ISO 527-2
Flexural Modulus (Compression Molded)	25.0	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	45.0	°C	ISO 306/A, ASTM D1525 ¹
Melting Temperature	84.0	°C	ISO 11357-3

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Sylvin 2990-75 Clear	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Sylvin 7868-90 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Moplen HP520M	LyondellBasell Industries	PP Homopolymer	Moplen
Ferro PP LPP30BV02NA	Ferro Corporation	PP, Unspecified	Ferro PP
Monprene® CP-11170 (PRELIMINARY DATA)	Teknor Apex Company	TPE	Monprene®