COSMOTHENE庐 F108-5
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOTHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NNSggc_COSMOTHENE-F108-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOTHENE F108-5 is specially design for excellent shrinkage, toughness and strength. F108-5 is not formulated with slip and antiblocking agent. Shrink film food packaging, heavy duty bag & etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 0.40 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 19.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Apparent Bending Modulus | 210 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 109 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (30.0 µm) | 100 | ASTM D2457 | |
| Haze (30.0 µm) | 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking (30.0 µm) | 20.0 | g/100 cm² | ASTM D3354 |
| Slip (30.0 µm) | 0.900 | Tan θ | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 155 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 175 | °C | |
| Melt Temperature | 190 | °C | |
| Die Temperature | 170 - 190 | °C |
| Extrusion instructions |
|---|
| Extruder: 50 mm diameter; L/D: 26; C.R: 3.4H Temperature: 200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® FU1007 | Covestro - Polycarbonates | PC | Makrolon® |
| McCann PP M30CCOO18 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| Generic TPU-Polyether | Generic | TPU-Polyether | Generic |
| Hifax CB 1128 A | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Osterlene® PPC-80-1.2-N | Osterman & Company | PP Impact Copolymer | Osterlene® |