CALIBRE™ 603-3
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NMpry6_CALIBRE-603-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 603-3 is a branched polycarbonate resin specially designed for extrusion of profiles, corrugated sheet and very complex multi-wall sheet. CALIBRE™ 603-3 offers a very high melt strength to calibrate effectively the most complex multi-wall sheet structures, such as a seven wall sheet or more, and to calibrate effectively complex profiles and corrugated sheet. CALIBRE™ 603-3 contains a UV absorber additive, but note that sheets for outdoor applications also require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 µm thick cap layer, using CALIBRE™ 320UV. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 62.0 | MPa | |
| Break | 66.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 90 | % | |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 16 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 80 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 126 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index 4 | IEC 60695-2-12 | ||
| 1.00 mm | 900 | °C | |
| 2.00 mm | 875 | °C | |
| 3.00 mm | 875 | °C | |
| Glow Wire Ignition Temperature 5 | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 775 | °C | |
| 3.00 mm | 775 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1360 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Sasol Polymers PE HR411/06 | Sasol Polymers | LLDPE | Sasol Polymers PE |
| HiFill® PA6 CM40 HS | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| ICORENE® 3940 | ICO Polymers NA, A Division of A. Schulman | LMDPE | ICORENE® |
| Sumiliteresin® PR-51732 | SBHPP | Phenolic | Sumiliteresin® |