ALCUDIA® HDPE TR-210
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NMAGgg_ALCUDIAHDPETR210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® TR210 is a high density polyethylene developed to provide excellent mechanical properties, toughness, good environmental stress cracking resistance (ESCR) and stability against oxidative degradation. This product provides a superior performance at high-speed extrusion together with a smooth surface finish of the cable. It is stabilized to be protected from thermal and shear degradation and contains a metal deactivator to ensure long-term ageing properties. TYPICAL APPLICATIONS Solid insulation of telephone single. Skin layer in foam-skin construction. Jelly-filled cable. ALCUDIA® TR210 can be extruded at a high melt temperature between 230°C - 260°C without risk of thermal or shear degradation. The optimum conditions depend on the application and the extrusion equipment used. When processed using proper extrusion conditions, ALCUDIA® TR210 is expected to meet the requirements of the following product and cable specifications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.943 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F50) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 700 | % | ISO 527-2 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Mechanical Properties 1(100°C) | > 75 | % | ISO 527-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 30 | min | EN 728 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Long Term Stability | 0 Failures | IEC 60811-4-2 | |
| Weight Gain - by gel absorption 2(70°C) | % | IEC 60811-4-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 3 | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 4.0E-4 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 - 260 | °C |
| Note Message | |
|---|---|
| 1 . | 10 days |
| 2 . | 10 days |
| 3 . | 0 Failures |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ E 310 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Ad-Tech Epoxy EC-426-2 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Clear-Flex® 95 | Smooth-On, Inc | PUR, Unspecified | Clear-Flex® |
| DINAPLEN® PPH1S10 M303-7035 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| KEBAFLEX® U A 85 EF B01 natural | BARLOG plastics GmbH | TPU, Unspecified | KEBAFLEX® |