Nylene® 609

Category: Nylon 6 , Polyamide 6
Manufacturer: Custom Resins Group
Trademark: Nylene®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: NM525n_Nylene-609.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
  • High viscosity, extrusion grade recommended for practically all types of extrusion including profile, film, and extrusion coating
  • Especially recommended for flexible packaging where as a film or coating it is used for the outside layer in multi-ply film constructions
  • Excellent melt flow and melt strength properties
  • Optimum processing conditions should permit for a melt temperature of 550 - 575°F at the die.
General Information
Features
  • Good Flow
  • Good Melt Strength
  • High Viscosity
Uses
  • Film
  • Packaging
  • Profiles
Processing Method
  • Extrusion
  • Extrusion Coating
  • Film Extrusion
  • Profile Extrusion
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.14g/cm³ASTM D792
MechanicalNominal ValueUnitTest Method
Tensile Strength (23°C)70.3MPaASTM D638
Tensile Elongation (Break, 23°C)140%ASTM D638
ImpactNominal ValueUnitTest Method
Notched Izod Impact (23°C)53J/mASTM D256
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load ASTM D648
    0.45 MPa, Unannealed 161°C
    1.8 MPa, Unannealed 62.2°C
Peak Melting Temperature 216°CASTM D3418
ExtrusionNominal ValueUnit
Die Temperature 288 to 302°C
Resin Grade Manufacturer Category Trademark
3M™ Dyneon™ Fluoroplastic THVP 2030GZ 3M Advanced Materials Division Fluorelastomer 3M™ Dyneon™ Fluoroplastic
Ad-Tech Epoxy EC-405 (50R/50H) Ad-Tech Plastic Systems Corp. Epoxy Ad-Tech Epoxy
DOMAMID® 6M40H DOMO Engineering Plastics SPA Nylon 6 DOMAMID®
Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-ACE Karina Ind. e Com. de Plásticos Ltda PVC, Unspecified Karina
LNP™ THERMOCOMP™ DX05475 compound SABIC Innovative Plastics PC LNP™ THERMOCOMP™