TECHNYL STAR™ S 216 V30 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NL2cCf_TECHNYL-STAR-S-216-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL STAR TM Polyamide, reinforced with 30% of glass fibre, for injection moulding. Characterized by a high fluidity of the melt. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.95 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9600 | 6200 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 180 | 110 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.3 | 5.5 | % | ISO 527-2/1A |
| Flexural Modulus | 9300 | 5200 | MPa | ISO 178 |
| Flexural Stress | 255 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 10 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | 81 | 90 | kJ/m² | ISO 179/1eU |
| -30°C | 50 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 12 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 82 | 65 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 204 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 3.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | -- | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.80 | 4.50 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 22 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 - 225 | °C | |
| Middle Temperature | 225 - 235 | °C | |
| Front Temperature | 235 - 245 | °C | |
| Mold Temperature | 80.0 | °C |
| Injection instructions |
|---|
| Inj Pressure vs Standard PA: -42%Spiral Length vs Standard PA: 220% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-278 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| SABIC® PP 622L | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| Chemieprene TPE ES-75NE | CP Chemie Resources (M) Sdn. Bhd. | SEBS+EPDM | Chemieprene |
| K-Bin Rigid PVC KB-6100 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| TECACOMP® PP ID blue 3956 | Ensinger GmbH | PP, Unspecified | TECACOMP® |