PRE-ELEC® TPE 1504
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NK7VdR_PRE-ELEC-TPE-1504.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® TPE 1504 is a highly conductive thermoplastic compound based on a thermoplastic elastomer (TPE). Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® TPE 1504 has retained the excellent mechanical properties of the base elastomer. Typical applications include extruded profiles, sheets and injection moulded technical parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.6 - 1.8 | % | ASTM D955 |
| Flow direction | 1.6 - 1.8 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 100% strain, 4.00mm | 350 | MPa | ASTM D638 |
| 200% strain, 4.00mm | 460 | MPa | ASTM D638 |
| 300% strain, 4.00mm | 550 | MPa | ASTM D638 |
| 100% strain, 4.00mm | 2.40 | MPa | ISO 527-2 |
| 200% strain, 4.00mm | 3.20 | MPa | ISO 527-2 |
| 300% strain, 4.00mm | 3.90 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | > 800 | % | ASTM D638 |
| Fracture, 4.00mm | > 800 | % | ISO 527-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 65.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Processing (Melt) Temp | 180 - 210 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Injection Pressure: Low to Medium |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 65.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 210 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 210°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2599 X 125737 C | RTP Company | PC+ABS | RTP |
| Viprene™ P85A-22U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| NYLOY® UB-0010N C35N2B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| HiFill® TPX-HTN-03002 A | Techmer Engineered Solutions | Nylon, Unspecified | HiFill® |
| THERMOLAST® K TC7HFZ (Series: UV/HF/SF) | KRAIBURG TPE | TPE | THERMOLAST® K |